Phase stable doped zirconia electrolyte compositions with low degradation

ABSTRACT

A solid oxide fuel cell (SOFC) includes a cathode electrode, a solid oxide electrolyte, and an anode electrode. The electrolyte and/or electrode composition includes zirconia stabilized with (i) scandia, (ii) ceria, and (iii) at least one of yttria and ytterbia. The composition does not experience a degradation of ionic conductivity of greater than 15% after 4000 hrs at a temperature of 850° C.

CROSS REFERENCE TO RELATED PATENT APPLICATION

This application is a continuation of U.S. application Ser. No.13/009,085, filed Jan. 19, 2011, which claims the benefit of U.S.Provisional Application No. 61/298,468, filed Jan. 26, 2010,incorporated herein by reference in their entirety.

BACKGROUND OF THE INVENTION

The present invention is generally directed to fuel cell components, andto solid oxide fuel cell electrolyte materials in particular.

Fuel cells are electrochemical devices which can convert energy storedin fuels to electrical energy with high efficiencies. Electrolyzer cellsare electrochemical devices which can use electrical energy to reduce agiven material, such as water, to generate a fuel, such as hydrogen. Thefuel and electrolyzer cells may comprise reversible cells which operatein both fuel cell and electrolysis mode.

In a high temperature fuel cell system, such as a solid oxide fuel cell(SOFC) system, an oxidizing flow is passed through the cathode side ofthe fuel cell while a fuel flow is passed through the anode side of thefuel cell. The oxidizing flow is typically air, while the fuel flow canbe a hydrocarbon fuel, such as methane, natural gas, pentane, ethanol,or methanol. The fuel cell, operating at a typical temperature between650° C. and 950° C., enables the transport of negatively charged oxygenions from the cathode flow stream to the anode flow stream, where theion combines with either free hydrogen or hydrogen in a hydrocarbonmolecule to form water vapor and/or with carbon monoxide to form carbondioxide. The excess electrons from the negatively charged ion are routedback to the cathode side of the fuel cell through an electrical circuitcompleted between anode and cathode, resulting in an electrical currentflow through the circuit. A solid oxide reversible fuel cell (SORFC)system generates electrical energy and reactant product (i.e., oxidizedfuel) from fuel and oxidizer in a fuel cell or discharge mode andgenerates the fuel and oxidant using electrical energy in anelectrolysis or charge mode.

Scandia stabilized zirconia (SSZ) SOFC electrolyte material exhibits ahigh oxygen ion conductivity. Typically, zirconia is doped with between8 and 11 mol % scandia (Sc₂O₃) in order to stabilize the cubic phasezirconia at high SOFC operating temperature of 650-850° C.

However, there are two problems with SSZ electrolyte materials: 1) theyexhibit a cubic to rhombohedral phase transformation at around 580° C.,and 2) the ionic conductivity slowly decreases with time, which is knownas ageing.

Others have shown that co-doping SSZ with one secondary rare earth oxidewill suppress the cubic to rhombohedral phase transformation. Forexample, 10Sc1Ce zirconia (10 mol % Sc₂O₃—1 mol % CeO₂—zirconia) and10Sc1Y (1 mol % Sc₂O₃—1 mol % Y₂O₃—zirconia) are examples of co-dopedzirconia compositions that do not exhibit the cubic to rhombohedralphase transformation.

However, both of these zirconia compositions still experience ageing(i.e., the a slow decrease in ionic conductivity with time at the SOFCoperating temperatures of 800-850C). Although the actual mechanism ofthis ageing degradation in ionic conductivity with time is not agreedupon in the scientific literature, one hypothesis is that the cubicphase is not stable and slowly decomposes into a tetragonal phase whichhas a lower ionic conductivity. The resulting material consists of atwo-phase mixture primarily of cubic phase with small domains (e.g., 2-5nm) of tetragonal phase. As shown in FIGS. 1 and 2, the 10Sc1Ce zirconiamay exhibit a faint superlattice of tetragonal phase as well as thecubic fluorite structure of zirconia.

SUMMARY OF THE INVENTION

One embodiment of the invention provides an electrolyte and/or electrodecomposition for a solid oxide fuel cell which includes zirconiastabilized with (i) scandia, (ii) ceria, and (iii) at least one ofyttria and ytterbia. Preferably, the at least one of yttria and ytterbiais present in an amount greater than 0 and equal to or less than 2.5 mol%.

Another embodiment of the invention provides a scandia stabilizedzirconia electrolyte composition for a solid oxide fuel cell, comprisinga formula (ZrO₂)_(1-w-x-z)(Sc₂O₃)_(w) (CeO₂)_(x) (Y₂O₃)_(a) (Yb₂O₃)_(b),where 0.09≦w≦0.11; 0<x≦0.025; a+b=z; 0≦z≦0.025; and x+z≧0.02. Anotherembodiment of the invention provides a scandia stabilized zirconiaelectrolyte composition for a solid oxide fuel cell, comprising aformula (ZrO₂)_(1-w-x-z)(Sc₂O₃)_(w) (CeO₂)_(x) (Y₂O₃)_(a) (Yb₂O₃)_(b),where 0.09≦w≦0.11; 0≦x≦0.0125; a+b=z, and 0.0025≦z≦0.02; and x+z≦0.02.

Another embodiment of the invention provides a method of operating asolid oxide fuel cell comprising a zirconia electrolyte stabilized withscandia and ceria. The method comprises operating the solid oxide fuelcell for at least 4000 hrs such that an electrolyte of the fuel celldoes not experience a degradation of ionic conductivity of greater than15%.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a contrast enhanced selected area electron diffraction patternof prior art 10Sc1Ce zirconia. The zone axis is of type <110> for cubiczirconia.

FIG. 2 is a contrast enhanced selected area electron diffraction patternof prior art 10Sc1Ce zirconia. The zone axis is of type <112> for cubiczirconia.

FIG. 3 is a graph showing ionic conductivity versus time for exemplaryand comparative examples of stabilized zirconia electrolytecompositions.

FIG. 4 is a cross-sectional view of a solid oxide fuel cell according toan embodiment of the invention and FIG. 5 is a side cross sectional viewof a SOFC stack according to an embodiment of the invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Without wishing to be bound by a particular theory, the presentinventors believe that the 10Sc1Ce composition is slightly under-dopedand is not fully stable (i.e., not sufficiently stabilized), and thus isprone to ageing due to the slow cubic to tetragonal phase decompositionor transformation at high temperature.

According to a first embodiment of the invention, the SSZ compositioncontains at least 2 molar percent of the additional stabilizing oxide(such as ceria, yttria and/or ytterbia) to provide sufficientstabilization to the SSZ composition to reduce or prevent the ageingdecomposition. The stabilizing oxide provides the stabilization of thecubic phase of SSZ and thus the suppression of the cubic to tetragonalphase transformation. According to a second embodiment, both ceria andat least one of yttria and ytterbia are added to the SSZ composition toreduce or prevent the ageing decomposition. The addition of both ceriaand at least one of yttria and ytterbia provides the stabilization ofthe cubic phase of SSZ and thus the suppression of the cubic totetragonal phase transformation. One exemplary composition of theseembodiments is zirconia has been co-doped with at least two additionalelements: 10Sc1Ce1Y (10 mol % Sc₂O₃—1 mol % CeO₂—1 mol % Y₂O₃—zirconia).According to a third embodiment, the SSZ composition has a coefficientof thermal expansion (“CTE”) close to that of interconnects which willbe used in a fuel cell stack with the SSZ electrolyte SOFCs. Theinterconnects may comprise chromium alloy interconnects having at least94 wt % Cr, 4-6 wt % Fe and 0-1 wt % Y. In a first aspect of the thirdembodiment, the SSZ composition contains greater than zero but less than2 mol % total of ceria, yttria and/or ytterbia, such as 1-2 mol % totalof ceria and at least one of yttria and/or ytterbia. By slightlyreducing the amount of at least one of ceria, yttria and/or ytterbia,the CTE of the electrolyte is increased such that it differs from theCTE of the interconnect by 10% or less, such as 5% or less, such as0-1%, without decreasing the stability or ageing degradation resistanceof the electrolyte. In a second aspect of the third embodiment, theyttria is replaced with ytterbia. It is believed that replacing yttriawith ytterbia should increase the CTE and ion conductivity of theelectrolyte material. Thus, the electrolyte compositions of the thirdembodiment are believed to exhibit improved beginning of life ionicconductivity, low degradation and higher CTE that is the same as orslightly different from a CTE of a Cr alloy interconnect. A decrease indifference in CTE between SOFC electrolytes and interconnects in a SOFCstack should result in decreased thermally induced stress and damage tothe stack components. Preferably, the electrolyte composition of allthree embodiments is homogeneous throughout its height, width andthickness rather than being a heterogeneous composite of yttria andscandia stabilized zirconias made by mixing of yttria and scandiastabilized zirconia powders.

Accordingly, the first embodiment of the invention provides a SOFCelectrolyte composition which comprises zirconia stabilized with (i)scandia, (ii) ceria, and (iii) at least one of yttria and ytterbia.Scandia may be present in an amount equal to 9 to 11 mol %, such as 10mol %, ceria may present in amount greater than 0 (e.g., at least 0.5mol %) and equal to or less than 2.5 mol %, such as 1 mol %, and atleast one of yttria and ytterbia may be present in an amount greaterthan 0 and equal to or less than 2.5 mol %, such as 1 mol %.

In one aspect of the first embodiment, the at least one of yttria andytterbia comprises yttria. In another aspect of the first embodiment,the at least one of yttria and ytterbia comprises ytterbia. In yetanother aspect of the first embodiment, the at least one of yttria andytterbia comprises both yttria and ytterbia. In this aspect, yttria maycomprise 0.5 to 1.5 mol % and ytterbia may comprise 1.5 to 0.5 mol % ofthe composition such that the total yttria and ytterbia content isgreater than 0.5 mol % and less than 2.5 mol %. The amount of scandia isgreater than the amount of ceria and the amount of the at least one ofyttria and ytterbia. The amount of ceria may be equal to, less than orgreater than the amount of the at least one of yttria and ytterbia.

In the second embodiment of the present invention, the amount ofstabilizing oxide, such as ceria, is at least 2 mol % to providesufficient stabilization to the SSZ composition to reduce or avoidageing. In this embodiment, the yttria and/or ytterbia is optionallyadded to the composition and may be omitted.

Thus, the SSZ electrolyte composition of both the first and the secondembodiment may have the formula (1):(ZrO₂)_(1-w-x-z)(Sc₂O₃)_(w)(CeO₂)_(x)(Y₂O₃)_(a)(Yb₂O₃)_(b)  (1),where w is from about 0.09 to 0.11, x is from greater than 0 to 0.025,the total of a and b equal to z, and z is from 0 to 0.025, and the totalof x plus z is greater than or equal to 0.02. In other words,0.09≦w≦0.11; 0<x≦0.025; a+b=z, and 0≦z≦0.025; and x+z≧0.02. Preferably,x ranges from 0.005 to 0.025, z ranges from 0.005 to 0.025, and thetotal of x and z is greater than or equal to 0.02 and less than or equalto 0.03. In other words, 0.005≦x≦0.025; 0.005≦z≦0.025; and0.02≦(x+z)≦0.03. More preferably, w=0.1; x=0.01; and z=0.01. Thus, w maybe about 10 mol %, x may be about 1 mol %, and z may be about 1 mol %.In formula (1), b may be less than a (i.e., b<a), a may be less than b(i.e., a<b), a may be equal to zero (i.e. a=0), b may be equal to zero(i.e., b=0), or a may be equal to b (i.e., a=b)

According to the third embodiment, the SSZ composition has a relativelyhigher coefficient of thermal expansion (“CTE”) close to that ofinterconnects which will be used in a fuel cell stack with the SSZelectrolyte SOFCs. The interconnects may comprise chromium alloyinterconnects having at least 94 wt % Cr, 4-6 wt % Fe and 0-1 wt % Y. Ina first aspect of the third embodiment, the SSZ composition containsgreater than zero but less than 2 mol % total of ceria and at least oneof yttria and/or ytterbia. For example, the SSZ composition contains 0.5to 1.75 mol % total, such as 0.5 to 1.5 mol % total, including 1 to 1.5mol % total of ceria and at least one of yttria and/or ytterbia. The SSZcomposition may contain 0.25 to 1.25 mol % ceria, such as 0.5 to 1 mol %ceria, and 0.25 to 1.25 mol %, such as 0.5 to 1 mol % of yttria,ytterbia or a combination of yttria and ytterbia. In a second aspect ofthe third embodiment, the yttria is replaced with ytterbia such that thecomposition contains substantially no yttria (e.g., an unavoidable traceamount of yttria or less than 0.1 mol % yttria). It is believed thatreplacing yttria with ytterbia should increase the CTE and ionconductivity of the electrolyte material. The SSZ composition maycontain 0 to 1.25 mol % ceria, such as 0.5 to 1 mol % ceria, and 0.25 to2 mol %, such as 0.5 to 1 mol % of ytterbia. The SSZ composition maycontain substantially no ceria (e.g., an unavoidable trace amount ofceria or less than 0.1 mol % ceria) if the composition contains at least0.75 mol % ytterbia, such as 1 to 2 mol % ytterbia, including 1 to 1.5mol % ytterbia. Thus, in the second aspect of the third embodiment, theelectrolyte composition for a solid oxide fuel cell includes zirconiastabilized with: (i) scandia present in an amount equal to 9 to 11 mol%, and (ii) ytterbia present in an amount equal to 1 to 2 mol %.

Thus, the SSZ electrolyte composition of the third embodiment may havethe formula (2):(ZrO₂)_(1-w-x-z)(Sc₂O₃)_(w)(CeO₂)_(x)(Y₂O₃)_(a)(Yb₂O₃)_(b)  (2),where w is from about 0.09 to 0.11, x is from 0 to 0.0125, a is from 0to 0.0125, b is from 0 to 0.02, the total of a and b equal to z, and zis from 0.0025 to 0.02, and the total of x plus z is less than or equalto 0.02. In other words, 0.09≦w≦0.11; 0≦x≦0.0125; a+b=z, and0.0025≦z≦0.02; and x+z≦0.02. Preferably, in the first aspect of thethird embodiment, x ranges from 0.0025 to 0.0125, such as 0.005 to 0.01,z ranges from 0.0025 to 0.0125, such as 0.005 to 0.01, and the total ofx and z is greater than or equal to 0.005 and less than or equal to0.0175, such as greater than or equal to 0.01 and less than or equal to0.015. In other words, 0.0025≦x≦0.0125, such as 0.005≦x≦0.01;0.0025≦z≦0.0125, such as 0.005≦z≦0.01, and 0.005≦(x+z)≦0.0175, such as0.01≦(x+z)≦0.015. More preferably, w=0.1; x=0.01 when z=0.005, andx=0.005 when z=0.01. Thus, w may be about 10 mol %, x may be about 0.5to 1 mol %, and z may be about 0.5 to 1 mol %. Preferably in the secondaspect of the third embodiment, x ranges from 0 to 0.0125, such as 0.005to 0.01, 0≦a≦0.001 (preferably a=0), and b and z range from 0.0025 to0.02, such as 0.005 to 0.01, and the total of x and z is greater than orequal to 0.005 and less than or equal to 0.02, such as 0.01 to 0.015. Informula (2), b may be less than a (i.e., b<a), a may be less than b(i.e., a<b), a may be equal to zero (i.e. a=0), b may be equal to zero(i.e., b=0), or a may be equal to b (i.e., a=b). Preferably, only one ofa or b equals zero. Exemplary compositions according to the thirdembodiment include:

-   10Sc1Ce1Y (10 mol % Sc₂O₃+1 mol % CeO₂+1 mol % Y₂O₃), remainder    zirconia;-   10Sc1Ce0.5Y (10 mol % Sc₂O₃+1 mol % CeO₂+0.5 mol % Y₂O₃), remainder    zirconia;-   10Sc1Ce1Yb (10 mol % Sc₂O₃+1 mol % CeO₂+1 mol % Yb₂O₃), remainder    zirconia;-   10Sc1Ce0.5Yb (10 mol % Sc₂O₃+1 mol % CeO₂+0.5 mol % Yb₂O₃),    remainder zirconia;-   10Sc0.5Ce0.5Y (10 mol % Sc₂O₃+0.5 mol % CeO₂+0.5 mol % Y₂O₃),    remainder zirconia;-   10Sc0.5Ce0.5Yb (10 mol % Sc₂O₃+0.5 mol % CeO₂+0.5 mol % Yb₂O₃),    remainder zirconia;-   10Sc0.5Ce1Y (10 mol % Sc₂O₃+0.5 mol % CeO₂+1 mol % Y₂O₃), remainder    zirconia;-   10Sc0.5Ce1Yb (10 mol % Sc₂O₃+0.5 mol % CeO₂+1 mol % Yb₂O₃),    remainder zirconia; and-   10Sc1Yb (10 mol % Sc₂O₃+1 mol % Yb₂O₃), remainder zirconia.

Embodiments of the electrolyte compositions have a high starting ionicconductivity of 0.14 S/cm or greater, preferably 0.15 S/cm or greater,such as 0.16 to 0.17 S/cm. The compositions of the present invention mayexperience less than 15% degradation in ionic conductivity with time,such as 0-15%, for example 0-10%, including 1-5%, in an air and/or in aH₂ containing environment after 4000 hours. Such minimization in ionicconductivity degradation may be due to stabilization of the cubic phaseleading to suppression of the cubic to tetragonal phase transformation.Additionally, at least one of the embodiments of the present inventionprovides an electrolyte composition wherein the composition does notexperience a cubic to rhombohedral phase transition at a temperature ofabout 25 to 850° C. In other words, the composition is cubic from roomtemperature to about 850° C. (i.e., the composition remains in the cubicphase from room to the SOFC operating temperature without generatingtetragonal domains over time or transforming to the rhombohedral phase).Therefore, compositions of the present invention do not experience adegradation of ionic conductivity of greater than 15% after 4000 hrs andat a temperature of 850° C.

For example, as shown in FIG. 3, conductivity measurements over time forcomparative and exemplary composition samples were performed at 850° C.The conductivity of the samples were measured using a DC 4-point methodwith the Van der Pauw geometry. The samples were tested in a test standcapable of high temperature and controlled gas environment. Measurementswere taken at 850° C. in either air or hydrogen environments. Theexemplary samples comprised compositions of zirconia stabilized with 10mol % of scandia, 1 mol % of ceria and 1 mol % of yttria (“10Sc1Ce1Y”).Conductivity measurements for one of the exemplary samples was conductedin a hydrogen atmosphere, and in air for the other sample. Thecomparative samples comprised compositions of zirconia stabilized with10 mol % scandia and 1 mol % ceria (“10Sc1Ce”). The conductivity of thecomparative compositions were measured in an air and a hydrogenatmosphere. As shown in FIG. 3, after 4000 hours, the comparativecompositions of 10Sc1Ce experienced significant degradation inconductivity with time, for example, a degradation of greater than about15%. However, the exemplary compositions of 10Sc1Ce1Y did not experiencea degradation of ionic conductivity of greater than 15% after 4000 hrsin either air or hydrogen.

The embodiments of the present invention may be utilized as anelectrolyte layer of a planar solid oxide fuel cell. In other words, thecomposition can be utilized as an electrolyte layer of a planar solidoxide fuel cell comprising an anode and a cathode. Preferably, thecomposition is used in an electrolyte supported cell where theelectrolyte layer supports the anode and cathode. For example, FIG. 4illustrates a solid oxide fuel cell 1 according to an embodiment of theinvention. The cell 1 includes an anode electrode 3, a solid oxideelectrolyte 5 and a cathode electrode 7. The electrolyte 5 may comprisea stabilized zirconia, such as zirconia stabilized with (i) scandia,(ii) ceria, and (iii) at least one of yttria and ytterbia, as describedabove. Alternatively, the electrolyte 5 may comprise an electrolytecomposition comprising formula (1) and any of the embodiments thatinclude the formula as described above.

A method of forming the planar, electrolyte supported SOFC 1 shown inFIG. 4 includes forming the cathode electrode 7 on a first side of aplanar solid oxide electrolyte 5 and forming the anode electrode 3 on asecond side of the planar solid oxide electrode. The anode and thecathode may be formed in any order on the opposite sides of theelectrolyte.

As shown in FIG. 4, the anode electrode 3 may contain one layer or aplurality of sublayers. Thus, the anode electrode 3 may contain a firstportion 13 and a second potion 23, each varying in composition andnickel content. For example, the first portion 13 is located between anelectrolyte 5 and the second portion 23. The first portion 13 of theanode electrode may contain nickel and a ceramic phase, such as astabilized zirconia and/or doped ceria, such as samaria doped ceria. Thesecond portion 23 of the anode electrode may also contain nickel and aceramic phase, such as a stabilized zirconia and/or doped ceria, such assamaria doped ceria. The first portion 13 may contain a lower ratio ofthe nickel containing phase to the ceramic phase than the second portion23 of the anode electrode. The cathode electrode 7 may comprise anelectrically conductive material, such as an electrically conductiveperovskite material, such as lanthanum strontium manganite (LSM). Otherconductive perovskites, such as LSCo, etc., or metals, such as Pt, mayalso be used. Compositions, orientations and configurations of thecathode and anode electrodes may comprise those discussed in co-pendingU.S. patent application Ser. Nos. 11/907,204 and 11/785,034 which arehereby incorporated by reference in their entirety herein.

In another embodiment of the invention, the composition of the first,second and/or third embodiment comprising a zirconia stabilized withscandia, ceria, and at least one of yttria and ytterbia may be used inan anode electrode, a cathode electrode, or both electrodes of the solidoxide fuel cell. Thus, the composition of the first, second and thirdembodiments may be used in any one, two or all three of the SOFC anode,cathode and electrolyte. In the composite anode and/or cathodeelectrodes, the stabilized zirconia of the first, second or thirdembodiments is used as the solid oxide ionic conducting phase, while anelectrically conductive material, such as a metal (e.g., nickel, copper,cobalt, platinum, palladium, etc. or their alloys) or an electricallyconductive ceramic (e.g., lanthanum strontium manganite (LSM), lanthanumstrontium cobaltite (La,Sr)CoO₃, lanthanum strontium cobalt ferrite(La,Sr)(Co,Fe)O₃, etc.,) is used as the electrically conducting phase.The degradation of ionic conductivity in the solid oxide ionicconducting phase of a composite electrode, such as the anode or cathode,will result in a degradation of the performance of the electrode.Therefore, composite electrodes containing a solid oxide ionicconducting phase with low ionic conductivity degradation, such as10Sc1Ce1Y, will exhibit lower degradation as compared to compositeelectrodes containing a ceramic material having a higher degradationrate.

For example, the zirconia stabilized with scandia, ceria, and at leastone of yttria and ytterbia may be used in a single layer or amulti-layer composite anode electrode. For example, the zirconiastabilized with scandia, ceria, and at least one of yttria and ytterbiamay be used in the first portion 13 and/or the second portion 23 of theanode electrode 3 described above. The first portion 13 of the anodeelectrode may contain nickel and the stabilized zirconia ceramic phase.The second portion 23 of the anode electrode may also contain nickel andthe stabilized zirconia ceramic phase. The first portion 13 may containa lower ratio of the nickel containing phase to the ceramic phase thanthe second portion 23 of the anode electrode. For example, the firstportion 13 of the anode electrode may contain a porosity of 5-30 volumepercent and a nickel phase content of 1 to 20 volume percent andremainder the stabilized zirconia ceramic phase. The second portion 23of the anode electrode may contain a higher porosity of 31 to 60 volumepercent, a nickel phase content of 21 to 60 volume percent and remainderthe stabilized zirconia ceramic phase. The nickel containing phase mayoptionally contain between 1 and 50 atomic percent, such as 5-30 at % ofan additional metal, such as cobalt and/or copper, and the balancenickel.

In another example, the cathode electrode 7 may comprise a compositecathode containing the electrically conductive phase, such as anelectrically conductive perovskite material (e.g., LSM) of 10 to 70volume percent and remainder porosity and the stabilized zirconiaionically conductive phase.

In another embodiment of the present invention, a method of operating asolid oxide fuel cell, for example, the fuel cell 1 of FIG. 4, comprisesoperating the fuel cell for at least 4000 hrs such that the SSZelectrolyte of the fuel cell does not experience a degradation of ionicconductivity of greater than 15%. Preferably, the electrolytecomposition is cubic from room temperature to about 850° C. and afteroperating at 850° C. for at least 4000 hours in air and hydrogen ambientprovided on the cathode and anode side of the electrolyte (i.e., thecomposition remains in the cubic phase from room temperature to the SOFCoperating temperature without generating tetragonal domains over atleast 4000 hours or transforming to the rhombohedral phase).

Fuel cell stacks are frequently built from a multiplicity of SOFC's 1 inthe form of planar elements, tubes, or other geometries. Fuel and airhas to be provided to the electrochemically active surface, which can belarge. The stack may comprise a plurality of planar or plate shaped fuelcells. The fuel cells may have other configurations, such as tubular.The stacks may be vertically oriented stacks or the fuel cells may bestacked horizontally or in any other suitable direction between verticaland horizontal. A plurality of interconnects are located in the stack,such that each fuel cell is located between two interconnects, and eachinterconnect acts as a gas separator plate, as described in the abovementioned U.S. application Ser. Nos. 11/907,204 and 11/785,034.

Frequently, the interconnect 9 which electrically connects the fuelelectrode 3 of one cell to the air electrode 7 of the adjacent cell isalso used as the gas flow separator plate 9, as shown in FIG. 5. The gasflow separator plate separates fuel, such as a hydrocarbon fuel, flowingto the fuel electrode (i.e., anode 3) of one cell in the stack fromoxidant, such as air, flowing to the air electrode (i.e., cathode 7) ofan adjacent cell in the stack. The separator 9 contains gas flowpassages or channels 8 between the ribs 10. In this case, the gas flowseparator plate which functions as an interconnect is made of orcontains electrically conductive material. An electrically conductivecontact layer, such as a nickel contact layer, may be provided betweenthe anode electrode and the interconnect. FIG. 5 shows that the lowerSOFC 1 is located between two gas separator plates 9.

The term “fuel cell stack,” as used herein, means a plurality of stackedfuel cells which share a common fuel inlet and exhaust passages orrisers. The “fuel cell stack,” as used herein, includes a distinctelectrical entity which contains two end plates which are connected topower conditioning equipment and the power (i.e., electricity) output ofthe stack. Thus, in some configurations, the electrical power outputfrom such a distinct electrical entity may be separately controlled fromother stacks. The term “fuel cell stack” as used herein, also includes apart of the distinct electrical entity. For example, the stacks mayshare the same end plates. In this case, the stacks jointly comprise adistinct electrical entity, such as a column. In this case, theelectrical power output from both stacks cannot be separatelycontrolled.

The foregoing description of the invention has been presented forpurposes of illustration and description. It is not intended to beexhaustive or to limit the invention to the precise form disclosed, andmodifications and variations are possible in light of the aboveteachings or may be acquired from practice of the invention. Thedescription was chosen in order to explain the principles of theinvention and its practical application. It is intended that the scopeof the invention be defined by the claims appended hereto, and theirequivalents.

The invention claimed is:
 1. A scandia stabilized zirconia electrolytecomposition for a solid oxide fuel cell, comprising; a formula(ZrO₂)_(1-w-x-b)(Sc₂O₃)_(w)(CeO₂)_(x)(Yb₂O₃)_(b), where: w=0.1; x=0.01and b=0.01; or w=0.1; x=0.01 and b=0.005; or w=0.1; x=0.005 and b=0.005;wherein: the scandia stabilized zirconia electrolyte compositionconsists of a single layer located in direct contact with an anode on afirst major surface of the single layer and in direct contact with acathode on a second major surface of the single layer; the compositiondoes not experience a degradation of ionic conductivity of greater than15% after 4000 hrs and at a temperature of 850° C.; the compositioncomprises a cubic phase which substantially lacks tetragonal phasedomains after operating in a solid oxide fuel cell at 850° C. for atleast 4000 hours in at least one of air or hydrogen ambient; and thecomposition does not experience a cubic to rhombohedral phase transitionat a temperature of about 25 to 850° C.
 2. The composition of claim 1,wherein: the composition is utilized as an electrolyte layer of a planarsolid oxide fuel cell comprising the anode and the cathode; theelectrolyte layer supports the anode and cathode; the solid oxide fuelcell is located in a solid oxide fuel cell stack adjacent to aninterconnect comprising at least 94 wt % Cr, 4-6 wt % Fe and 0-1 wt % Y;and a coefficient of thermal expansion of the electrolyte differs by 1%or less from a coefficient of thermal expansion of the interconnect. 3.The composition of claim 1, wherein w=0.1; x=0.01 and b=0.01.
 4. Thecomposition of claim 1, wherein w=0.1; x=0.01 and b=0.005.
 5. Thecomposition of claim 1, wherein w=0.1; x=0.005 and b=0.005.
 6. A scandiastabilized zirconia electrolyte composition for a solid oxide fuel cell,comprising a formula (ZrO₂)_(1-w-x-b)(Sc₂O₃)_(w)(CeO₂)_(x)(Yb₂O₃)_(b),where: 0.09≦w≦0.11; 0.005<x<0.015 and 0.0025<b≦0.015; wherein: thescandia stabilized zirconia electrolyte composition consists of a singlelayer located in direct contact with an anode on a first major surfaceof the single layer and in direct contact with a cathode on a secondmajor surface of the single layer; the composition does not experience adegradation of ionic conductivity of greater than 15% after 4000 hrs andat a temperature of 850° C.; the composition comprises a cubic phasewhich substantially lacks tetragonal phase domains after operating in asolid oxide fuel cell at 850° C. for at least 4000 hours in at least oneof air or hydrogen ambient; and the composition does not experience acubic to rhombohedral phase transition at a temperature of about 25 to850° C.
 7. The composition of claim 6, wherein: 0.01≦x≦0.015 and0.005≦b≦0.0125.
 8. The composition of claim 7, wherein: 0.005≦b≦0.01. 9.The composition of claim 8, wherein: w=0.1, b=0.01 and x=0.01.
 10. Thecomposition of claim 6, wherein: 0.005≦x≦0.0125 and 0.0025≦b≦0.01. 11.The composition of claim 6, wherein: 0.0025≦b≦0.0125.
 12. Thecomposition of claim 11, wherein: 0.005≦x≦0.01 and 0.005≦b≦0.01.
 13. Thecomposition of claim 8, wherein: w=0.1 and x=0.01.
 14. A planar fuelcell comprising the electrolyte of the composition of claim
 6. 15. Ascandia stabilized zirconia electrolyte composition for a solid oxidefuel cell, comprising: a formula(ZrO₂)_(1-w-x-b)(Sc₂O₃)_(w)(CeO₂)_(x)(Yb₂O₃)_(b), where w=0.1; x=0.01and b=0.01; wherein: the scandia stabilized zirconia electrolytecomposition consists of a single layer located in direct contact with ananode on a first major surface of the single layer and in direct contactwith a cathode on a second major surface of the single layer; thecomposition experiences a degradation of ionic conductivity of 1-5%after 4000 hrs and at a temperature of 850° C.; the compositioncomprises a cubic phase which substantially lacks tetragonal phasedomains after operating in a solid oxide fuel cell at 850° C. for atleast 4000 hours in at least one of air or hydrogen ambient; and thecomposition does not experience a cubic to rhombohedral phase transitionat a temperature of about 25 to 850° C.
 16. The composition of claim 15,wherein the composition have a starting ionic conductivity of 0.14 S/cmor greater.
 17. The composition of claim 16, wherein the compositionhave a starting ionic conductivity of 0.16 to 0.17 S/cm.